modular hip implants, cobalt-alloy, implant failure, fracture




Biomaterials | Biomedical Engineering and Bioengineering | Engineering


Two modular hip implants with a cobalt-alloy head and a cobalt-alloy stem were retrieved after a fracture had occurred in the neck region of the femoral component, eighty-five and seventy months after implantation. Both implants failed less than one millimeter distal to the taper junction between the head and the stem (outside of the taper). The fracture surfaces of the implant were investigated with the use of scanning electron microscopy, to determine the nature of the failure process. The fractures occurred at the grain boundaries of the microstructure and appeared to be the result of three factors: porosity at the grain boundaries; intergranular corrosive attack, initiated both at the head-neck taper and at the free surface; and cyclic fatigue-loading of the stem. The corrosive attack of the free surface was initiated, in part, by the egression of surface grains and by the ingression of fluid into the intergranular regions. Sectioned surfaces showed extensive intergranular corrosive attack in the prosthetic neck localized in the region of the head-neck taper junction and penetrating deeply into the microstructure.

Creative Commons License

Creative Commons Attribution 3.0 License
This work is licensed under a Creative Commons Attribution 3.0 License.

Included in

Biomaterials Commons



To view the content in your browser, please download Adobe Reader or, alternately,
you may Download the file to your hard drive.

NOTE: The latest versions of Adobe Reader do not support viewing PDF files within Firefox on Mac OS and if you are using a modern (Intel) Mac, there is no official plugin for viewing PDF files within the browser window.